ISO 14104-2017 齒輪--磨光后的表面回火侵蝕檢查--化學(xué)法 Gears — Surface temper etch inspection after grinding, chemical method

This document specifies procedures and requirements for the detection and classification of localized overheating on ground surfaces by chemical etch methods. The process described in this document is typically used on ground surfaces; however, it is also useful for the detection of surface anomalies that result from post-heat treatment machining such as hard turning, milling and edge breaking (deburring) processes. Surface metallurgical anomalies caused by carburization or decarburization are also readily detectable with this process. Some methods which have been used in the past are no longer recommended. Specifications are intended to be changed to use the methods in this document. These etching methods are more sensitive to changes in surface hardness than most hardness testing methods. This document applies to steel parts such as gears, shafts, splines and bearings. It is not applicable to nitrided parts and stainless steels. NOTE This process, although at times called “nital etch”, is not intended to be confused with other processes also known as “nital etch”. The surface temper etch procedure is performed after grinding and before additional finishing operations such as superfinishing, shot peening and honing.rd edition 2017-04 Gears — Surface temper etch inspection after grinding, chemical method Engrenages — Contr？le par attaque chimique des zones surchauffées lors de la rectification Reference number ISO 14104:2017(E) ？ ISO 2017 ISO 14104:2017(E) COPYRIGHT PROTECTED DOCUMENT ？ ISO 2017, Published in Switzerland All rights reserved. Unless otherwise spe